Abstract
SiC fiber reinforced titanium aluminides matrix composites based on TiAl (Ti–43Al–9V) were fabricated by means of matrix-coated fiber method through hot isostatic pressing. Microstructure of the SiCf/Ti–43Al–9V interfacial reaction zone in the composites was identified by means of scanning electron microscopy and transmission electron microscopy. The results show that three types of reaction products TiC, Ti2AlC and (Ti,V)5(Si,Al)3 are formed between carbon coating of SiC fiber and the matrix. TiC is adjacent to the carbon coating of the SiC fiber, and (Ti,V)5(Si,Al)3 is close to the matrix. Ti2AlC layer exists as columnar grains between TiC and (Ti,V)5(Si,Al)3 layers. The TiC layer can be divided into fine-grained layer and coarse-grained layer. The fine-grained TiC layer contains amorphous carbon, and the coarse-grained TiC layer is separated from fine-grained TiC by an intermittent carbon layer. In addition, TiC particles are also formed between carbon coating and SiC. Furthermore, the formation mechanism of the interfacial reaction products was discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.