Abstract

The objective of this study was to survey the influence of poly(acrylic acid-co-butyl acrylate) [P(AA-co-BA)] branches on the sizing properties (i.e., paste stability, adhesion, properties of film and sized warps) of biological macromolecule (corn starch) for further promoting the properties of bromoisobutyryl esterified starch (BBES) and developing a new biobased sizing agent [BBES-g-P(AA-co-BA)]. The sizing properties of BBES-g-P(AA-co-BA) were estimated in comparison with acid-hydrolyzed starch (AHS) and BBES. Compared with the two starches, BBES-g-P(AA-co-BA) displayed higher paste stability, bonding forces to both polyester and polyester/cotton roving, film elongation and water solubility, as well as lower film strength. And the increased grafting ratio exhibited positive effects on these properties of BBES-g-P(AA-co-BA). The properties containing increase in strength, loss in extension, abrasion resistance and hairiness of polyester and polyester/cotton blended yarns sized with BBES-g-P(AA-co-BA), were superior to those sized with AHS and BBES, respectively, indicating that the incorporation of P(AA-co-BA) branches onto BBES could further promote the sizing qualities of both yarns. The BBES-g-P(AA-co-BA) with a grafting ratio of 16.51 % was concluded to size both yarns for improvement of yarn quality.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.