Abstract
Bismuth telluride (Bi2Te3)-based thermoelectric materials are well-known for their high figure-of-merit (zT value) in the low-temperature region. Stable joints in the module are essential for creating a reliable device for long-term applications. This study used electroless Co-P to prevent a severe interfacial reaction between the joints of solder and Bi2Te3. A thick and brittle SnTe intermetallic compound layer was successfully inhibited. The strength of the joints improved, and the fracture mode became more ductile; furthermore, there was no significant degradation of thermoelectric properties after depositing the Co-P layer after long-term aging. The result suggests that electroless Co-P could enhance the interfacial stability of the joints and be an effective diffusion barrier for Bi2Te3 thermoelectric modules.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.