Abstract
Enhancement of a flexible poly(vinyl chloride) (PVC)-silica composite interface was studied by the application of γ-aminopropyltrimethoxysilane on silica. Composites containing silica and silanized silica up to 25.6 phr (per hundred resin) and prepared by sol-gel technology were subjected to water and water vapor attacks similar to that in their daily use. Silane application resulted in diminishing liquid water and water vapor sorption by about 24.0% and 11.9%, respectively. Equilibrium weight gain values of the composites having different amounts of silica correlated well with a peak at 3400 cm-1 in the IR spectra which was attributed to the stretching vibration of the O-H group of water. Liquid water and water vapor diffusivities in composites determined by the evaluation of weight gain against time data were about 0.4 x 10-13 and 0.4 x 10-12 m2 s-1, respectively. Inhibition of dioctyl phthalate (DOP) migration from composites by silane application was also determined as 24% using UV measurements. The m...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.