Abstract
Ta/NiO/NiFe/Ta multilayers were prepared by rf reactive and dc magnetron sputtering. The exchange coupling field between NiO and NiFe reached 120 Oe. The composition and chemical states at the interface region of NiO/NiFe were studied using the x-ray photoelectron spectroscopy (XPS) and peak decomposition technique. The results show that there are two thermodynamically favorable reactions at NiO/NiFe interface: NiO+Fe=Ni+FeO and 3NiO+2Fe=3Ni+Fe2O3. The thickness of the chemical reaction as estimated by angle-resolved XPS was about 1–1.5 nm. These interface reaction products are magnetic defects, and we believe that the exchange coupling field Hex and the coercivity Hc of NiO/NiFe are affected by these defects.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.