Abstract
Multilayered heterostructures of Ce0.85Sm0.15O2-δ and Y0.16Zr0.92O2-δ of a high crystallographic quality were fabricated on (001)-oriented MgO single crystal substrates. Keeping the total thickness of the heterostructures constant, the number of ceria-zirconia bilayers was increased while reducing the thickness of each layer. At each interface Ce was found primarily in the reduced, 3+ oxidation state in a layer extending about 2 nm from the interface. Concurrently, the conductivity decreased as the thickness of the layers was reduced, suggesting a progressive confinement of the charge transport along the YSZ layers. The comparative analysis of the in-plane electrical characterization suggests that the contribution to the total electrical conductivity of these interfacial regions is negligible. For the smallest layer thickness of 2 nm the doped ceria layers are electrically insulating and the ionic transport only occurs through the zirconia layers. This is explained in terms of a reduced mobility of the oxygen vacancies in the highly reduced ceria.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.