Abstract
Infrared (IR) spectra were collected on a series of blends of poly(lactic acid) (PLA) and poly(3-hydroxybutyrate- co-3-hydroxyhexanoate) (P(3HB- co-3HHx) (3HHx=13.4 mol%)) using a single-bounce temperature-controlled attenuated-total-reflection (ATR) accessory with a diamond internal reflection element (IRE). Different approaches were used to analyze the raw spectral data, including peak positions, widths and intensities, principal components, and 2D correlation spectra. Differences in the interactions between the functional groups of the components become apparent as a function of temperature and composition. This study provides insights into the submolecular-level interactions and miscibility of this polymer blend system. In particular for the 40/60 PLA/P(3HB- co-3HHx) blend, two types of crystalline P(3HB- co-3HHx) CO bands were observed. The band representing a more-ordered local CO environment had a peak absorbance at a lower wavenumber than the second, less-ordered CO species. The 2D IR correlation analysis also revealed that the more-ordered material disappeared first upon heating of the sample and the amorphous P(3HB- co-3HHx) CO band formed before the less-ordered P(3HB- co-3HHx) CO band disappeared. This observation is likely the result of the less-ordered crystalline form being replenished by thermally induced disordering of the more-ordered crystalline form. Thus, the less-order crystalline material may be viewed as an intermediate form during the melting process. In the 80/20 PLA/P(3HB- co-3HHx) blend, it was observed that the lower wavenumber peak in the PLA CO doublet preferentially interacts with amorphous P(3HB- co-3HHx). When 10–20% P(3HB- co-3HHx) is added to PLA, the crystallinity of P(3HB- co-3HHx) is restricted, probably due to domain size restriction and inherent low nucleation density. These IR results suggest that P(3HB- co-3HHx) has the potential to increase the toughness of PLA dramatically, thereby enlarging the design space of sustainable materials achievable by blending.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.