Abstract
Hydroxy-terminated polybutadiene/isophorone diisocyanate (HTPB/IPDI) polyurethane rubber which was aged in air at elevated temperatures has been studied by infrared microspectroscopy. Spectra were collected in transmission mode on microtomed samples. Analysis of sets of spectra taken across the sectioned material showed that most of the degradation occurred in the polybutadiene part of the polymer and that the urethane linkage was essentially unchanged. The trans isomer of the polybutadiene appears to be preferentially degraded compared with the vinyl isomer. The IR technique does not provide significant information about the cis isomer. The IR spectra indicated that likely degradation products included acids, esters, alcohols, and small amounts of other products containing a carbonyl functional group. Band area ratios, supported by a principal components analysis, were used to derive degradation profiles for the material. These profiles were steep-sided indicating an oxygen diffusion limited process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.