Abstract
In this paper, Ti–C–N nanocomposite films are deposited under different nitrogen flow rates by pulsed bias arc ion plating using Ti and graphite targets in the Ar/N2 mixture gas. The surface morphologies, compositions, microstructures, and mechanical properties of the Ti–C–N films are investigated systematically by field emission scanning electron microscopy (FE-SEM), x-ray photoelectron spectroscopy (XPS), grazing incident x-ray diffraction (GIXRD), Raman spectra, and nano-indentation. The results show that the nanocrystalline Ti(C,N) phase precipitates in the film from GIXRD and XPS analysis, and Raman spectra prove the presence of diamond-like carbon, indicating the formation of nanocomposite film with microstructures comprising nanocrystalline Ti(C,N) phase embedded into a diamond-like matrix. The nitrogen flow rate has a significant effect on the composition, structure, and properties of the film. The nano-hardness and elastic modulus first increase and then decrease as nitrogen flow rate increases, reaching a maximum of 34.3 GPa and 383.2 GPa, at a nitrogen flow rate of 90 sccm, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.