Abstract
The CuCrSn alloy is promising as a high-strength and high-conductivity Cu alloy due to its relatively low smelting requirement. However, thus far investigations into the CuCrSn alloy are still quite lacking. In this study, the microstructure and properties of Cu-0.20Cr-0.25Sn (wt%) alloy specimens prepared under different rolling and aging combinations were comprehensively characterized, in order to reveal the effects of cold rolling and aging on properties of the CuCrSn. The results show that increasing the aging temperature from 400 °C to 450 °C can noticeably accelerate precipitation, and cold rolling before aging significantly increases its microhardness and promotes precipitation However, the deformation hardening is eliminated during the aging process, making the microhardness decrease monotonically when the aging temperature and the cold rolling ratio before aging are high. Performing cold rolling after aging can maximize precipitation strengthening and deformation strengthening, and the adverse impact on its conductivity is not serious. A tensile strength of 506.5 MPa and a conductivity of 70.33% IACS were obtained by such a treatment, whereas only the elongation decreases a little. Different strength-conductivity combinations of the CuCrSn alloy can be achieved through appropriate design of the aging and post-aging cold rolling conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.