Abstract
In this study, effect of cooling rate on the microstructure and corrosion behavior of the solution-treated 1.4462 alloy was investigated. 1.4462 alloy was heat-treated at 1000 °C, 1120 °C and 1200 °C for different duration in order to obtain various phase balance. Two different cooling regimes (rapid cooling and steady cooling) were applied following the solution treatment processes. Also, effect of sigma phase was investigated together with ferrite and austenite phases for steady cooled samples. After heat treatment processes, samples were characterized by an optical microscope (OM), image analysis and scanning electron microscope (SEM). Moreover, hardness tests and electrochemical corrosion tests were applied. According to results, Ferrite ratio and ferrite grain size were increasing with increasing solution treatment temperature and time. Also, ferrite phase was more dominant compared to sigma phase for hardness of the solution-treated samples. Moreover, existing of sigma in higher amount promoted the observation of Epit value.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.