Abstract
The physicomechanical properties and thermodynamic stability of segmented polyether urethane containing poly(tetramethylene oxide) segments of different molecular masses (М ∼ 1000, 1400, 1950) and plasticized with di(2-ethylhexyl) sebacate were analyzed in relation to the molecular mass of the soft segments, and the glass transition point of the soft phase of the polymer was determined. Based on the results obtained, a rapid method was suggested for experimental determination of the osmotic pressure (up to ∼1000 kPa) in the polymer–plasticizer system. The possibilities of preparing thermodynamically stable plasticized materials of high strength (up to 22–26 MPa) with the glass transition point as low as–95 to–100°С were demonstrated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.