Abstract
Under identical and judiciously pre-optimized synthesis conditions, the influence of different combinations of zirconium sources and/or post treatment conditions on structural properties, thermal stability, phase composition and morphology of zirconia has been investigated. High surface area tetragonal zirconia could be synthesized in a cost-effective manner from 1M solution of zirconium oxy-nitrate at pH 11 using aqueous ammonia solution as a precipitant when calcined at 400°C for 3h. Irrespective of the preparation method, pH and starting precursor, zirconia samples prepared without digestion contained dominant monoclinic phase with some traces of tetragonal phase when calcined at 700°C. Even though there is linear decrease in surface area with increase in the crystallite size for each sample as a function of calcination temperature, no co-relation between the surface area and crystallite size could be achieved. SEM images show agglomerated and irregular shape particles between 10 to 20μm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.