Abstract
The fracture toughness of alloy HT-9, † † HT-9 is a product of the Sandvikens Jernverks AB, Sweden. a martensitic stainless steel under consideration for fast reactor and fusion reactor applications, was determined from circular compact tension specimens using the multi-specimen R-curve method. Specimens with thicknesses of 11.94, 7.62 and 2.54mm and widths of 23.88 and 11.94 mm were tested to investigate the effects of specimen size on fracture toughness. The test results obtained from all specimens are in good agreement and thickness requirements for a valid J 1 c test are satisfied. The experiment indicates that small specimens of HT-9 may be used for post-irradiation fracture toughness testing. Fractographic examination of the fracture surfaces reveals that fracture in HT-9 is significantly influenced by delta ferrite stringers present in the material. The fracture surface examination and crack opening displacement measurements for specimens tested at various temperatures are consistent with the temperature dependence of the J 1 c results.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.