Abstract
In order to investigate the influence of shot peening on the surface durability of case-hardened steel gears, the case-hardened steel gears shot-peened with different shot velocities and shot diameters were fatigue-tested using a power circulating type gear testing machine. The hardness, the compressive residual stress and the surface roughness of the gears were increased by shot peening. The cause of failure of all the test gears was pitting due to surface cracking. The surface durability of the gear shot-peened under medium condition in this experimental range was higher than that of the non-peened gear. On the other hand, that of lightly or strongly shot-peened gear was just as high. Judging from the pmax-N curves and also the [A(σy/HV)]max-N curves, it is denoted in this experimental range that the surface durability of case-hardened steel gears was influenced by the hardness and the surface roughness of the gears. Therefore, it is proposed in this experimental range that the medium shot peening condition, that is, 60m/s shot velocity and 0.6mm shot diameter, should be selected in order to improve the surface durability of case-hardened steel gears.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Advanced Mechanical Design, Systems, and Manufacturing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.