Abstract
Functionalization of composite materials by ionizing radiation is considered an environmentally friendly technology to improve the compatibility of natural fibers with a polymer matrix. However, depending on the dose, it might also cause degradation. In particular, the effect of ionizing radiation on hybrid polymer composites reinforced with both naturals and synthetics fibers still needs more attention. In the present work, for the first time, the mechanical behavior of a hybrid polyester composite reinforced with 33wt% of curaua fibers mat and 7wt% of aramid fabric subjected to ultraviolet (UV) and gamma ionizing radiation, was investigated. Ultraviolet exposure for 300 and 600h and gamma radiation doses of 150 and 300kGy were applied before 3 points bending tests. The results disclose an increase in flexural strength and modulus with increasing UV when compared to other irradiated conditions. Macroscopic observation and scanning electron microscopy analysis of fractured irradiated specimens revealed delamination as the main failure mechanism.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.