Abstract
The influence of different types of cemented carbide blades and thickness of TiAlN/a-C:N and TiN/AlTiN protective coatings used in the wood industry on cutting performance has been studied. Three types of WC-Co cemented carbide blades with different cobalt content were used in the study. The thicknesses of both types of coatings were ~2 and ~5 µm. The structure, chemical and phase composition were studied using transmission and scanning electron microscopy (TEM, SEM), X-ray dispersion spectroscopy (EDX) and X-ray diffraction (XRD), respectively. The adhesion was evaluated by scratch test. Nanohardness and durability tests of uncoated and coated blades were performed. We found that the blades covered with 5 µm TiN/AlTiN coatings exhibited the best durability characteristic. The cutting distances were within the range ~6700-~7080 depending on the substrates in comparison with pure substrates (~4300–~4900) and 2 µm TiN/AlTiN coatings (~5400–~6600). The presence of a thin and soft outer a-C:N layer aggravates the nanohardness and durability of the coated blades.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.