Influence of different annealing process on the giant magneto-impedance(GMI) effect in soft magnetic alloy films of(Fe88Zr7B5)0.96Cu0.04,which were prepared by radio frequency(RF) sputtering,was studied.It is obtained that both natural and current annealing can reduce the longitudinal GMI ratio.And the longitudinal GMI ratio of the annealed films increases with the increase of annealing current,and reaches a maximum value of 17% at 800mA,while the sensitivity increase to 7%(kA/m)-1 at such annealing current(800mA).In addition,influence of the magnetic field annealing on GMI effect is discussed.It is found that both the longitudinal and transverse GMI ratios of the films after magnetic field annealed increase at different temperatures.There exists a critical temperature(250℃),at which the longitudinal GMI ration presents a single-peak with a value of 17.5%,while the transverse one presents a double-peak with a value of 17.8% at ±0.4kA/m.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.