Influence of Ca[(Li1/3Nb2/3)0.8Ti0.2]O3‐δ filler on the microwave dielectric properties of polyethylene and polystyrene for microelectronic applications

Abstract

AbstractCeramic reinforced polyethylene and polystyrene composites were prepared by melt mixing and hot molding techniques. Temperature stable low‐loss Ca[(Li1/3Nb2/3)0.8Ti0.2]O3‐δ (CLNT) ceramic was used as the filler to improve the dielectric properties of the polymers. The relative permittivity and dielectric loss in the microwave frequency range were increased with increase in the ceramic loading. As the filler content increased from 0 to 0.50 volume fraction, the relative permittivity increased from 2.3 to 9 and dielectric loss tangent from 0.0006 to 0.005 for polyethylene‐CLNT composite. In the case of polystyrene‐CLNT composite, the relative permittivity and dielectric loss tangent increased from 2.1 to 10.5 and 0.0005 to 0.0032 respectively with increase in filler content from 0 to 0.50 volume fractions. The thermal stability of the relative permittivity of polymer ceramic composites was also investigated. The experimentally observed relative permittivity was compared with theoretical models. POLYM. ENG. SCI., 2010. © 2009 Society of Plastics Engineers