Abstract
A series of TaVN–Ag nanocomposite films were deposited using a radio-frequency magnetron sputtering system. The microstructure, mechanical properties, and tribological performance of the films were investigated. The results showed that TaVN–Ag films were composed of face-centered cubic (fcc) TaVN and fcc-Ag. With increasing Ag content, the hardness of TaVN–Ag composite films first increased and then decreased rapidly. The maximum hardness value was 31.4 GPa. At room temperature, the coefficient of friction (COF) of TaVN–Ag films decreased from 0.76 to 0.60 with increasing Ag content from 0 to 7.93at%. For the TaVN–Ag films with 7.93at% Ag, COF first increased and then decreased rapidly from 0.60 at 25°C to 0.35 at 600°C, whereas the wear rate of the film increased continuously from 3.91 × 10−7 to 19.1 × 10−7 mm3/(N·mm). The COF of the TaVN–Ag film with 7.93at% Ag was lower than that of the TaVN film, and their wear rates showed opposite trends with increasing temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.