Abstract
ABSTRACTSpent nuclear fuel in the U.K. is stored within ponds dosed with NaOH in order to inhibit corrosion and, to ensure the efficiency of storage regimes, there is a need to define and quantify the corrosion processes involved during immersion of fuel cladding. In this project, state-of-the-art characterisation techniques were employed to image the corroding surfaces of two nuclear fuel cladding materials: stainless steel and Magnox. Advanced gas-cooled reactor fuel cladding consists of 20Cr-25Ni-Nb stabilised stainless steel and during irradiation the microstructure of the cladding undergoes significant changes, including grain boundary element depletion and segregation. High-speed atomic force microscopy with nanoscale resolution, enabled precipitates and pit initiation in stainless steel to be imaged. Magnox is a magnesium–aluminium alloy and during irradiation in a reactor the outer metal surface oxidises, forming an adherent passive layer which subsequently hydrates when exposed to water. Corrosion processes encompass breakdown of passivity and filiform-like corrosion, both of which were imaged in situ using the scanning vibrating electrode technique.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.