Abstract
To improve the shape memory effect, the solutionized Fe-24Mn-6Si-9Cr-6Ni alloy was shot peened and subsequently annealed. The phase constituent was examined using the X-ray diffraction method. Microstructure evolution was characterized using an optical microscope and the electronic backscatter diffraction method, and the shape memory effect was evaluated using a bending test. The results show that α′-martensite and ε-martensite were introduced into the shot-peened surface layer. The α′-martensite remained after annealing even at 850 °C. Microstructure of the surface layer was refined through shot peening and subsequent annealing. Compared with those of the solutionized specimen, the shape recovery ratio and recovery strain of the specimens that are shot peened and subsequently annealed are significantly improved at different prestrains.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.