Abstract
The zone-leveling Czochralski (ZLCz) technique is a continuous feeding process and can be used for the growth of near-stoichiometric lithium niobate (SLN) single crystals. However, the finite crucible length can cause the variation of the zone length and thus the composition and stoichiometry, especially in the growth of a large diameter crystal. To solve the problems, several approaches were proposed for the growth of 4 cm-diameter 1 mol% MgO-doped SLN. The modification of the hot zone to minimize the zone variation was found useful for the uniformity, but the stoichiometry was inadequate even with the zone composition up to 60 mol% Li 2O. A Li-excess feed was further used and a good Li/Nb ratio was obtained. Adding K 2O (16 mol%) into the solution zone was useful as well, but it was inferior to using the Li-excess feed. In addition, a much lower growth rate was needed for getting an inclusion-free crystal.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.