Abstract
Al 2O 3/Ti 3SiC 2 multilayer materials with high mechanical properties in terms of bending strength and work of fracture have been prepared by in situ hot-pressing at 1600 °C for 4 h. In order to further improving the mechanical properties, SiC whiskers were added to Al 2O 3 layers as the 2nd-level toughening agent. With the content of SiC whisker increasing, the bending strength and work of fracture showed a similar trend of increasing firstly and then decreasing. Hence, the optimal mechanical properties of 688 MPa for bending strength and 2583 J/m 2 for work of fracture were obtained when the added content of SiC whisker was 20 wt%. These excellent properties should be attributed to 1st-level toughening mechanism (multilayer structural toughening), 2nd-level toughening mechanism (whisker toughening), and the synergy effect between them. Hence, adding SiC whiskers was an effective approach to improving the mechanical properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.