Abstract
Abrasion wear rates of conventional and two-step austempered ductile cast iron (ADI) were investigated. Conventional austempering and two-step austempering processes were carried out at 280, 300, and 320°C. Microstructures revealed that higher austemperig temperature resulted in coarser ausferrite and higher volume fractions of blocky retained austenite. The ausferrite in two-step austempered ADI was slightly coarser comparing to the coventional ADI since the temperature was raised by 30°C during austempering. Two-body abrasion wear rates of ADIs were studied using a Suga abrasion wear tester. It was found wear rates of the two-step ADI become significantly lower than those of the conventional ADI, especially when the austempering was carried out at low temperature, i.e. 280°C. Such behavior was due to the strong influence of high carbon concentration in retained austenite eventhough the ausferrite matrix was coarser.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.