Abstract
The hydrogen flux of Pd–Ru membranes was investigated after they were exposed to H2S at different concentrations and over various period of time. The membranes were characterized by XPS, XRD, SEM, and hydrogen permeation tests. The Pd–Ru membrane exhibits excellent sulfur tolerance. The results show that when exposed to 10–80 ppm H2S at 723 K for 7 h, the hydrogen flux remains 57–73%. After removal of 10 ppm H2S, 100% recovery of flux is observed, and the flux recovers to 94% and 89% for membranes exposed to 30 ppm and 50 ppm H2S, respectively. Irreversible flux loss occurs when the membranes are exposed to 80 ppm H2S for 7 h or 30 ppm H2S for 72 h. The combination of SEM, XRD and XPS results shows that the presence of Ru on the surface significantly prevents the sulfidation of Pd. The initial rapid decrease in hydrogen flux appears to be mainly due to the blocking of surface sites, exacerbated by the subsequent formation of chemically adsorbed sulfur compounds. The high temperature annealing in H2 decomposes the chemically adsorbed species.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.