Abstract
ABSTRACTMelamine formaldehyde microsphere (MF) was incorporated into nitrile butadiene rubber (NBR) and styrene butadiene rubber (SBR), respectively. The interaction between MF and rubber and effects of interfacial interaction on the dispersion of filler in rubber matrix, dynamic mechanical analysis, vulcanisation characteristics and kinetics were studied. The results showed that MF interacted with NBR through hydrogen bonds while there had no observed interaction between MF and SBR. The parameter b of MF/NBR calculated by the ratio of modulus and strains increased significantly, which demonstrated further the strong interaction between MF and NBR. For MF/SBR system, however, the parameter b changed slightly with little polymer–filler interaction. The Scanning Electron Microscope images released that strong polymer–filler interaction caused the uniform dispersion of MF in NBR matrix. The vulcanisation of MF/rubber was fitted by Ghoreishy’s model, and the addition of MF increased the rate of curing, shear modulus of compound and activity energy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.