Abstract
Due to its ferroelectricity, hafnium oxide has attracted a lot of attention for ferroelectric memory devices. Amongst different dopant elements, zirconium is found to be beneficial due to the relatively low crystallization temperature of hafnium‐zirconium‐oxide (HZO), thus it is back‐end‐of‐line (BEoL) compatible. The thickness of HZO has a significant impact on ferroelectric device reliability. High operation temperatures and high endurance are important criteria depending on the application. Herein, various HZO thicknesses (7, 8, and 10 nm) in MFM (metal‐ferroelectric‐metal) capacitors are investigated at varying operation temperatures (25 to 175 °C) at varying electric fields (±3 to ±5.4 MV cm−1) with respect to polarization, leakage current, endurance, and retention. 7 nm HZO showed promising results with an endurance of 107 cycles, with a low leakage current density, and almost no retention loss after 10 years. Extrapolated results at operation conditions (±2 MV cm−1 and 10 MHz) showed an endurance of 1010 cycles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.