Abstract
In this study, the microstructure and corrosion resistance of the stir zone (SZ) of the AA2198-T8 Al-Cu-Li alloy welded by friction stir welding (FSW) were investigated by microscopy, immersion tests and electrochemical techniques such as measurements of open circuit potential variation with time, and scanning vibrating electrode technique (SVET) measurements. A low chloride-containing solution (0.005 mol L−1 NaCl) was employed in the corrosion studies and severe localized corrosion (SLC) was observed in the SZ related to intergranular attack. The results were compared to those of the non-affected areas by FSW, also known as base metal (BM). In the BM, SLC was found and the type of attack related to it was intragranular. In both zones, BM and SZ, SLC was due to precipitates of high electrochemical activity, specifically T1 (Al2CuLi) phase in the BM, whereas TB (Al7Cu4Li) / T2 (Al6CuLi3) in the SZ. Scanning vibrating electrode technique (SVET) analysis was very useful in the study of SLC in the AA2198-T8 alloy showing the development of high anodic current densities at the mouth of the SLC sites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.