Abstract
Zirconium diboride (ZrB2) is a material of particular interest because of the excellent and unique property combination of high melting point, high electrical and thermal conductivity. In this work, the effect of addition of beta-silicon carbide (β-SiC) on hot pressing sintering of ZrB2 was investigated. Four compositions were studied with 0, 10, 20 e 30 vol% of SiC. ZrB2 powder and mixtures were prepared by planetary milling with SiC spheres during 4 h. Samples were sintered at 1850 °C/1h with a pressure of 20 MPa in argon atmosphere. β-SiC has undergone phase transformation to α-SiC during sintering. The addition of SiC increased densification with increasing of SiC content. The total densification of sample was 96.8 % of theoretical density for sample with 30 vol% of SiC and Vickers hardness was 19.9 ± 0.3 GPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.