Yb3+-doped Lu2O3 nanoparticles produced by laser ablation were used to fabricate transparent ceramics by a combination of pressureless sintering in vacuum (PS) followed by a hot isostatic pressing (HIPing). The samples were subjected to various PS and HIPing conditions and the microstructure evolution and its correlation with the transmittance were investigated. Relative densities of over 97% were achieved after PS at the temperatures of 1250–1700 °C. Rapid grain growth occurred within PS and HIPing temperatures above 1500 °C leading to formation of intragranular porosity which is deleterious for optical quality. Higher transmittance (81.7% at λ = 1080 nm) and ultrafine microstructure with an average grain size of 0.35 μm were obtained by PS at 1250 °C followed by HIPing at 1400 °C for 5 h under 207 MPa. Output power of 2.02 W with a slope efficiency of 46.5% was obtained under a quasi-continuous wave end pumping at 929.4 nm.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.