Abstract
The corrosion behavior of alloy Ni 201 in molten sodium hydroxide (NaOH) at 600 °C was investigated at varying basicity levels of the molten NaOH. The ability for Ni 201 to form passivating oxides was investigated after immersion tests varying from 70 to 340 h under atmospheres of argon and argon with different partial pressure of water. Morphology and thicknesses of the corrosion products were characterized by Scanning Electron Microscopy (SEM) and crystallography of the corrosion products by X-ray Diffraction (XRD). Dynamic polarizations were made to investigate the effects of basicity and electrochemical potential.The results showed that Ni 201 corroded at a reduced rate in molten acidic NaOH compared to neutral NaOH due to the formation of NiO. The oxide scales formed on Ni 201 in acidic NaOH were shown to grow non-parabolically and did not result in full corrosion protection as the oxide scales showed crack development over time.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.