Abstract
Specimens of powder fabricated by codeposition of zirconium and yttrium nitrates with the using special dry ing techniques and regranulation by the method of hot isostatic pressing have been tested in air allowing for the laws of compaction of granulated powder at a final firing temperature of about 1500°C. The resulting ma terial had the following properties: a density p = 5.91 g/cm (98% of the theoretical value), an ultimate bend ing strength a = 1100 MPa, and a crack resistance K = 19.5 MPa . rn A set of the specimens was sub jected to hot isostatic pressing after natural sintering and exhibited the following properties: p = 6.08 g/cm = 1400 MPa, K = 17.5 MPa · m1/2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.