Abstract
The nanodispersed NaTi2(PO4)3/C composite containing 20–25 wt.% of in-situ formed carbon, was synthesized by gel combustion procedure followed by a heat treatment at 650, 700 and 750 °C. The samples calcined at 700 and 750 °C displayed crystalline nasicon structure. They were subjected to the investigation of intercalation/deintercalation kinetics in aqueous NaNO3 and LiNO3 solutions, using cyclic voltammetry and galvanostatic charging/discharging measurements. As regards to the effect of electrolyte composition, the reactions were evidenced to be roughly twice faster in sodium nitrate than in lithium nitrate solution. Among the samples treated at 700 and 750 °C, better performance was evidenced for the sample treated at lower temperature. Coulombic capacity in NaNO3 solution at charging rate 1C amounted to ∼70 mAh g−1 and ∼55 mAh g−1 for the sample calcined at 700 and 750 °C, respectively, and displayed surprisingly slight dependence on charging rate up to even 100C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.