Abstract
High magnetostriction (λ) and coupling coefficient (dλ/dH) of 315 ppm and 1.97×10−9 A−1m, respectively, are obtained at room temperature for sintered cobalt ferrite derived from nanocrystalline powders. Also, the powder was compacted at a low pressure of 8 MPa and sintered for a short duration of 10 min at 1450 °C. Magnetic annealing at 300 °C in a field of 0.5 T for 30 min further enhanced the magnetostriction coefficient to 345 ppm with a higher coupling coefficient 2.12×10−9 A−1m. The magnetic field above which maximum magnetostriction is observed is reduced by almost half after magnetic annealing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.