Abstract
Lath-like silicon oxynitride crystals have often been observed in the microstructure of silicon nitride based ceramics after processing. They are usually located in glassy regions which are siliceous solidified sintering aid liquid, and usually contain a small (∼100nm) a-Si3N4 crystal. These nitride crystals are considered to be seeds, incompletely dissolved in the melt, that are heterogeneous nucleation sites for the oxynitride crystals. We present here the first observations of morphological and crystallographic habits between the seed nanocrystals and the host oxynitride laths.Fig. 1 shows a typical oxynitride lath containing a nitride seed crystal. The lath is surrounded by glass and ß-Si3N4 particles, and a small cristobalite particle (a minor constituent). This microstructure is from an Si02-Si3N4 ceramic processed with Al2O3 sintering aid. The same oxynitride lath/seed structures were observed when other sintering aids (eg. Y2O3, MgO, ZrO2) were used, so they are independent of sintering aid.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.