Abstract
Heat Treatment and Alloying of Spherulitic Graphite Cast Iron for Intensification of Properties
Highlights
Ductile Iron is likewise ordinarily known as "Nodular Iron" or Spheriodial graphite (S.G) iron was licensed in 1948
Mechanical Properties The mechanical properties measured by using Universal testing machine and greyensions of specimen was carried out according to ASTM (A 370-2002), are castn in Table 3 and Table 4,lists the mechanical properties of tensile strength, yield stress, elongation and hardness of ductile ironsN1, N2 respectively
Extension for Austempered Ductile Iron (ADI) is The following observations were acquired tentatively expanding from 0.5 hr. to 1.0 hr. with slight amid Austempering heat treatment diminished from 1.0 hr. to 2.0 hr. as appeared in figure 4.c and 5.c, which demonstrates I)
Summary
Ductile Iron is likewise ordinarily known as "Nodular Iron" or Spheriodial graphite (S.G) iron was licensed in 1948. Experiments have shown that proper heat treatment methods can improve the properties of Cast Iron. EXPERIMENTAL TECHNIQUE The experimental procedure for the project work can be listed as: Preparation of Specimen, Tensile test, Heat treatment process, Hardness test, Study of mechanical properties and study of Microstructure.
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Trend in Scientific Research and Development
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.