Abstract

Precise control of the heteroepitaxy on a low-cost foreign substrate is often the key to drive the success of fabricating semiconductor devices in scale when a large low-cost native substrate is not available. Here, we successfully synthesized three different phases of Ga2O3 (α, β, and e) films on c-plane sapphire by only tuning the flow rate of HCl along with other precursors in an MOCVD reactor. A 3-fold increase in the growth rate of pure β-Ga2O3 was achieved by introducing only 5 sccm of HCl flow. With continuously increased HCl flow, a mixture of β- and e-Ga2O3 was observed, until the Ga2O3 film transformed completely to a pure e-Ga2O3 with a smooth surface and the highest growth rate (∼1 μm/h) at a flow rate of 30 sccm. At 60 sccm, we found that the film tended to have a mixture of α- and e-Ga2O3 with a dominant α-Ga2O3, while the growth rate dropped significantly (∼0.4 μm/h). The film became rough as a result of the mixture phases since the growth rate of e-Ga2O3 is much higher than that of α-Ga2O3...

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.