Abstract
Alkaline phosphatase (ALP) was sucessfully incorporated into the halloysite (HAL) nanotubes, as confirmed by FTIR-ATR and XRD analyses. The loading efficiency (LE) of ALP was found to be 13.5%, while its encapsulation efficiency (EE) was estimated to be around 27%, as determined using the Bradford test. The influence of the immobilization in HAL on the enzyme activity was measured using standard ALP activity assay. Immobilized ALP effectively induced the bomineralization process, as showed by SEM, EDS, and XRD studies. As a result, calcium phosphate was produced in the form of hydroxyapatite cauliflower-like structures, with a slight content of calcium hydroxide. Interestingly, the encapsulation of ALP guest molecules in the HAL nanotubes considerably increased its thermal stability, most probably due to the heat sink effect. The activity of HAL-bound ALP was also found to be pH-independent in the wide range of pH values (3-10) due to the amphoteric nature of the aluminum oxide lining the HAL nanotube internal surface. Due to an increased resistance to the unfavorable conditions, which are often encountered during scaffold preparation or sterilization, ALP-HAL nanocomposite material may constitute an attractive bioactive component of the scaffolds for bone regeneration.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.