High-quality (Pb, La)(Ti, Zr)O3 films were grown on n-GaN. The film thickness ranged from 0.5 to 5 μm. The material was prepared by a chemical solution method with compositions of 8/65/35 and 0/52/48. The films grown on GaN buffered with a thin layer of indium in oxide were highly textured and exhibited excellent ferroelectric properties with Pr=20–26 μC/cm2. A large field-induced birefringence of 0.025 was measured in the film with a composition of 8/65/35 under a field strength of 2×105 V/cm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.