Abstract
High-density and uniformly aligned tungsten oxide nanotip arrays have been deposited by a conventional thermal evaporation on ITO glass substrates without any catalysts or additives. The temperature of substrate was 450–500 °C. It was shown that the tungsten oxide nanotips are single-crystal grown along [0 1 0] direction. For commercial applications, field emission of the tungsten oxide nanotip arrays was characterized in a poor vacuum at room temperature. The field emission behaviors are in agreement with Fowler–Nordheim theory. The turn-on field is 2.8 V μm −1 as d is 0.3 mm. The excellent field emission performances indicated that the tungsten oxide nanotip arrays grown by the present approach are a good candidate for application in vacuum microelectronic devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.