Abstract
ZnCdSe/BeZnTe II–VI compound superlattices (SLs) were grown on InP substrates by molecular beam epitaxy for the first time. In the X-ray diffraction studies, definite satellite peaks were observed for each sample, which indicates that fine periodic SL structures were obtained. For SL samples with several layer thickness combinations, wide-range visible emissions from 740 to 507 nm were observed during photoluminescence (PL) studies at 15 K. Comparison of PL emission properties at 15 K for a ZnCdSe/BeZnTe SL and ZnCdSe bulk samples showed the superior emission intensity of the SL sample. A double hetero-structure (DH) consisting of ZnCdSe/BeZnTe SLs and BeZnTe cladding layers was fabricated. In the PL spectrum of the DH sample at 15 K, sharp emission peaks at 517 and 604 nm were observed. Visible light emitting diodes were fabricated by applying ZnCdSe/BeZnTe SLs as the active layer, and were evaluated under pulsed current injections at room temperature. A single-peak yellow-green emission around 562 nm was obtained.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.