Abstract
AbstractThe floating zone growth of magneto‐optical crystal YFeO3 has been investigated. The polycrystalline feed rod was prepared by a pressure of 250MPa and sintering at about 1500°C. A crack‐ free YFeO3 single crystal has been successfully grown. The crystal preferred to crystallize along <100> direction with about 10° deviation. The X‐ray rocking curve of the crystal has a FWHM of 24 arcsec, confirming the high crystal quality of the sample. The (100) plane was etched by hot phosphoric acid and the dislocation density was about 104/cm2. A thin outer layer with Y2O3‐rich composition was found at the periphery of as‐grown crystals, which was attributed to the Fe2O3 evaporation during growth. (© 2007 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.