Abstract
Despite the increased attention devoted to exploring cathode construction based on various nitrogen-enriched carbon scaffolds at room temperature, the low-temperature behaviors of Li-S cathodes have yet to be studied. Herein, we demonstrate the good low-temperature electrochemical performances of nitrogen-enriched carbon/sulfur composite cathodes. Electrochemical evaluation indicates that a reversible capacity of 368 mAh g(-1) (0.5 C) over 100 cycles is achieved at -20 °C. After returning to 25 °C, a capacity of 620 mAh g(-1) (0.5 C) is achieved over 350 cycles with a low-capacity attenuation rate (0.071% per cycle) and an initial capacity of 1151 mAh g(-1) (0.1C). This positive electrochemical property was speculated to result from the good surface chemistry of the various amine groups in the nitrogen-enriched carbon materials with enhanced polysulfide immobilization.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.