Abstract
This study compared the relative fracture toughness of a Bis-GMA//TEGDMA (50:50 wt%)-based resin system modified by 5, 10, and 15 wt% of a methacrylate-terminated poly(butadiene-acrylonitrile-acrylic acid) terpolymer toughening agent. After storage in distilled water at 37 +/- 2 degrees C for 7 days, plane strain fracture toughness (KIC) was determined on an Instron testing machine at a 0.5-mm min-1 displacement rate. The glass transition temperature (Tg) in degrees C was determined after 7 days (dry and wet) storage by thermomechanical analysis. The results of this study showed significantly improved fracture toughness and lowered water sorption with the modified resin systems which was indicated by higher wet glass transition temperatures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.