Abstract
GdAlO 3 and Al 2O 3 powders were mixed and pulverized using ball mills. The prepared powder was sintered by SPS at 1450 °C without holding time. SEM observation of the sintered specimen showed a eutectic-like microstructure. This is called ‘pseudo-eutectic’ in this research. The microstructure formed from a powder pulverized by a tumbling ball mill for one week was much finer than that by a planetary ball mill for 5 and 10 h. The fine homogeneous eutectic-like (pseudo-eutectic) microstructures could be formed at both eutectic and off-eutectic compositions. In case of crystallization from a melt of eutectic components, homogeneous eutectic microstructures can be formed only at restricted compositions very close to the eutectic one. Coarse primary crystals generally exist in the eutectic microstructure at off-eutectic compositions. The pseudo-eutectic microstructures can be formed at any compositions because a mixing ratio of the starting powders can be varied.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.