Abstract
AbstractPolymeric porous membranes were prepared from polytetrafluoroethylene (PTFE) fine powder by a series of mechanical operations, such as extrusion, rolling, and stretching. The structure of the prepared porous membrane was well characterized by a spatial periodicity of nodes (domain of agglomerated PTFE particles) and fibril domains. The fibrils were highly oriented in the direction of the stretching operation, providing pores in the polymeric membrane as slit‐like voids between adjoining fibrils. The unit size of the periodic structure varied depending on the number averaged molecular weight of PTFE and the stretching conditions, the temperature of stretching, and the stretching rate and stretching ratio. A fibril consisted of several thread‐like structures that were easily formed between PTFE particles due to the rolling operation in parallel with their direction. The dependence of the steady tensile stress in the stretching operation on the PTFE molecular weight was much weaker than that presumed for noncrystalline polymeric systems. The activation energy of 11.3 kJ/mol for the growth of fibrils was only several times as large as the thermal energy at the ambient temperature. These results imply that the thread‐like structures can easily be pulled out of PTFE particles. This view is in accordance with the previously proposed microstructure in PTFE particles.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.