An amorphous phase was formed for (Fe0.75Pt0.25)100−xBx (x=25 and 30) alloys by melt-spinning. Their crystallization temperature were 671 and 667 K, respectively. The amorphous alloys exhibited good soft magnetic properties. The crystallized structure consisted of γ1-FePt (fct), Fe2B and γ-FePt (fcc) phases, and their average grain sizes were about 15 nm after annealing at 785 K for 900 s. The remanence (Br), reduced remanence (Mr⁄Ms), coercivity (iHc) and maximum energy product (BH)max were 0.96 T, 0.83, 340 kA/m and 102.2 kJ/m3, respectively, for the 25 at%B alloy, and 0.91 T, 0.82, 368 kA/m and 96.5 kJ/m3, respectively, for the 30 at%B alloy. The reversible demagnetization loop behavior was also confirmed. Consequently, the good hard magnetic properties are interpreted as resulting from exchange magnetic coupling among nanoscale hard γ1-FePt and soft Fe2B and γ-FePt magnetic phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.