Abstract
The n-type Sn2TiO4 phase was synthesized using flux methods and found to have one of the smallest visible-light bandgap sizes known that also maintains suitable conduction and valence band energies for driving photocatalytic water-splitting reactions. The Sn2TiO4 phase was synthesized using either a SnCl2 flux or a SnCl2/SnF2 peritectic flux in a 2:1 flux-to-precursor ratio heated at 600 and 400 °C for 24 h, respectively. The two types of salt fluxes resulted in large rod-shaped particles at 600 °C and smaller tetragonal prism-shaped particles at 400 °C. Surface photovoltage spectroscopy measurements produced a negative photovoltage under illumination >1.50 eV, which confirmed electrons as the majority charge carriers and ∼1.50 eV as the effective band gap. Mott–Schottky measurements at pH 9.0 showed the conduction (−0.54 V vs NHE) and valence band (+1.01 V vs NHE) positions meet the critical thermodynamic requirements for total water splitting. The Sn2TiO4 particles were deposited and annealed as polycry...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.