Abstract
ZnS nanocrystals were prepared via chemical precipitation method and characterized by X-ray diffraction (XRD), Transmission electron microscopy (TEM), ultraviolet-visible (UV-vis) and photoluminescence (PL) spectra. The results indicated that the ZnS nanocrystals have cubic zinc blende structure and diameter is 3.68 nm as demonstrated by XRD. The morphology of nanocrystals is spherical measured by TEM which shows the similar particle size. The photoluminescence spectrum peaking at about 424 nm was due mostly to the trap-state emission, and a satellite peak at 480nm ascribed to the dangling bond of S in the surface of ZnS nanocrystals. The emission intensity of ZnS was enhanced after ultraviolet irradiation, the enhancement of the Photoluminescence intensity was due to the elimination of the surface defects after ultraviolet irradiation, for the growth of the coated shell on ZnS nonacrystals, the Photoluminescence intensity was increased as ultraviolet irradiation time growth, finally tends to be stable for the surface state of nanocrystals steady.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.